General Properties of T-Rip HDPE sheet material.
|
s.#
|
Test
|
UOM
|
Value
|
Test Method
|
|
1
|
Material
|
|
HDPE
|
|
|
2
|
Density
|
g/cm3
|
0.92
|
ASTM D 1505
|
|
3
|
Melt index (190 deg. C, 5kg. wt.)
|
g/10min
|
≤0.69
|
ASTM D 1238
|
|
Melt index (190 deg. C,2.16kg.wt)
|
g/10min
|
≤1.00
|
ASTM D 1238
|
|
4
|
Tensile strength at yield
|
MPa
|
>15
|
ASTM D 638
|
|
Tensile strength at break
|
MPa
|
>24
|
ASTM D 638
|
|
5
|
Elongation at yield
|
%
|
19.5
|
ASTM D 638
|
|
Elongation at break
|
%
|
700
|
ASTM D 638
|
|
6
|
Carbon Black content
|
%
|
2.25
|
ASTM D 1603
|
|
7
|
Water absorption
|
%
|
≤0.02
|
ASTM D 570
|
|
8
|
Sheet Dimensions
Thickness
width
length
|
mm
mm
mtr
|
1.5-5±0.005
1100
As required
|
ASTM D 4801
|
|
9
|
Sheet color
|
|
Black or other colors
|
|